How is the galvanizing line made

A lot of metal products that use now are handled through hot dip galvanization process, such product is corrosion-resistant performance is good, apply in different environment, won't suffer easily corrode, service life is lengthened. Compared with common metal products, such galvanized products are required. Use a lot of metal wire, metal wire galvanization processing can get galvanization line, the result is better.

 How does the process of converting ordinary wire into galvanized wire? Above all should check metallic line appearance, cannot have oily, those who have a lot of oily also is unqualified product, cannot undertake galvanization process. Metal lines must be straightened, not bent, the outside surface of the uneven corrosion can not be galvanized. The wire to be hot-dip galvanized shall not have a label attached to the outside. The pickling water of the metal line is prepared by adding water with hydrochloric acid. The pickling of galvanization line is not a time, see specific circumstance undertakes pickling for many times, and want regular vibration.

 At the end of the pickling process, the solvent is treated, and the wire is put into the solvent tank and soaked completely into the solvent. Soak in solvent for 1 to 2 minutes, keep solvent temperature at room temperature, and keep solvent clean. Dry after solvent treatment is qualified, put the metal wire on the drying receiving rack, dry the metal surface moisture, and pay attention to not too high drying temperature. After drying, it is an important process of hot galvanizing. Dip the metal wire into the molten zinc liquid for reaction. The zinc alloy coating with uniform adhesion indicates the completion of the galvanizing line.